Mohr's theory of failure utilizes the well-known stress circle and the envelope of a family of circles as criteria for failure of materials subject to biaxial or triaxial stress. Thus Mohr's theory predicts that failure of materials is due to failure in shear, whereas Griffith's theory postulates that it is due to failure at crack tips.