The increase in size that sometimes occurs when a refractory raw material or product is fired; it is usually expressed as a linear percentage expansion from the dry to the fired state. Firing expansion can be caused by a crystalline conversion (e.g., of quartz into cristobalite, or of kyanite into mullite plus cristobalite), or by bloating.